Silane crosslinked PE Insulating Compounds

Silane crosslinked PE Insulating Compounds

The silane crosslinked PE insulating compounds are made mainly from LDPE together with proper additive such as silane crosslinking agent, initiator, anti-oxidant and copper-resistant agent through mixing and granulation. YJG-3(101C, 101B) and YJWG-10(201C, black) are the 2-stage process silane crosslinked products, where A is the grafting component and B the masterbatch of catalyst and the mixing ratio of A:B is 95:5. These compounds are good in workability, excellent in performances, and simple in both the technological process and the operation, which are suitable for the overhead cables and low voltage cables up to 10kV as well as the control cables, as shown below:

YJG-3(101C) Silane-XLPE Compound of Sioplas Method for wires and cables up to 3kV (Natural)

Send Inquiry

S/N	Testing item	Unit	Standard	Typical value
1	Tensile strength	MPa	≥13.5	24
2	Elongation	%	≥350	450
3	Brittleness temperature    Testing temperature    Brittle capability	°CFail number	-76≤15/30	0
4	Aging in airCircumstance:temperature             timeChange of tensile properties≤Change of elongation ≤	°Ch%%	135±2168±20±20	+5-3
5	Hot set elongation    200°C,0.2MPa,15min    Elongation under load    Permanent deformation after cooling	%%	≤100≤5	500
6	Gel content	%	≥60	65
7	DC volume resistivity at 20°C	Ω·m	≥1.0×1014	1.0×1015
8	Dielectric strength	MV/m	≥25	38
9	Dielectric constant 50Hz, 20 °C			2.2
10	Dielectric loss factor 50Hz, 20 °C			3×10-4

Note:product standard JB/T 10437-2004 XLPE compounds for wires and cables

Silane crosslinked PE Insulating Compounds